Injection

Hon Hamn can produce various sorts of plastic products and the largest injection machine is 1300 TON.

UL / ISO 9001 certified Plastic Injection Factory.

All injection machines had equipped with Robot Arms for higher safety, higher efficiency, and more stable production.

Central Conveying and Auto Feeding System to provide Clean and Automatic Controlled injection molding.
Equipment List
-
VP80H
80 QTY: 1 -
VP81K
81 QTY: 1 -
VP100
100 QTY: 1 -
VP130G
130 QTY: 1 -
VP130M
130 QTY: 1 -
VP180
180 QTY: 1 -
VP180G
180 QTY: 2 -
VP250E
250 QTY: 1 -
VP250F
250 QTY: 1 -
VP350
350 QTY: 1 -
HTF120
120 QTY: 1 -
HTF380
380 QTY: 4 -
HTF470
470 QTY: 1 -
HTF600
600 QTY: 1 -
JU13000
1300 QTY: 1 -
VP-35
35 QTY: 1 -
CY 1000STDM
120 QTY: 1 -
RHCM BT120S
QTY: 1
: Take Out Robots
Steel
FEATURES | THERMAL | ||||
GENERIC | COMMON NAME | HEAT DISTORTION TEMPERATURE | CONTINOUS HEAT TEMPERATURE | THERMAL EXPANSION COEFFICIENT | HEAT TRANSFER ARC RESISTANCE |
Test Mode | ASTM | D648 | Long Time | D696 | CI77 |
Units | ℃(46kg/cm2) | ℃ | 105/℃ | 10-4cal Sec cm /℃ cm | |
PVC | 氯乙烯 | 80 | 65-75 | 7-25 | 3.0-7.0 |
CPVC | 氯乙烯 | 95-112 | 99 | 6.8-7.6 | 3.3 |
HDPE | 聚乙烯 | 43-54 | 80 | 11-13 | 11-12.4 |
UPE | 乙烯鋼 | 91 | 120 | 12 | 11-12.4 |
PVDF | 鐵氟龍2F | 160 | 150 | 12 | 3 |
PTFE | 鐵氟龍4F | 240-245 | 290 | 10 | 6 |
PETP | 聚酯膠 | 180 | 100 | 2.2 | 3.36 |
PP | 聚丙烯 | 99-104 | 85 | 6-8.5 | 2.8 |
AP-6 | 尼龍6 | 67-70 | 79-121 | 8.3 | 5.85 |
AP-66 | 尼龍66 | 66-104 | 82-150 | 8 | 5.885 |
MC | MC尼龍 | 149-219 | 121-149 | 9 | X |
FEATURES | THERMAL | ||||
GENERIC | COMMON NAME | HEAT DISTORTION TEMPERATURE | CONTINOUS HEAT TEMPERATURE | THERMAL EXPANSION COEFFICIENT | HEAT TRANSFER ARC RESISTANCE |
Test Mode | ASTM | D648 | Long Time | D696 | CI77 |
Units | ℃(46kg/cm2) | ℃ | 105/℃ | 10-4cal Sec cm /℃ cm | |
POM | 塑膠鋼 | 110 | 80-120 | 8.5 | 5.5 |
PPS | 聚苯橕硫 | 230 | 220 | ||
PU | 優力膠 | ||||
PSU | 聚硐 | 180 | 150 | ||
PBI | 聚苯並咪唑 | ||||
PI VESPEL | 聚酰亞胺 | ||||
ABS | 丁二烯 | 94-107 | 60-110 | 6-13 | 4.6-8.6 |
PMMA | 壓克力 | 74-102 | 71-85 | 5-9 | 4-6 |
PC | 聚碳酸酯 | 130-140 | 120 | 6.6 | 4.6 |
PEEK | 聚醚醚酮 | 250 | 160 | 1.4 | 2.2 |
BAKELITE | 電木 | X | 150 | 1.4 | 4.9 |
FRP | 玻璃纖維 | 139-278 | 180 | 1.1-3.5 | 4-10 |
FEATURES | PHYSICAL | ||||||
GENERIC | COMMON NAME | PROPORTION | IN THEIR ORIGINAL APPEARANCE | WATER ABSORPTION | CHANGES WHEN EXPOSED TO LIGHT | MACHINABILITY | YUDEN RATE |
Test Mode | ASTM | D790 | Common Materials | D572 | D150 | ||
單位 | Target | 24Hrs % | 1KHz | ||||
PVC | 氯乙烯 | 1.45 | Gray | 0.07-0.4 | easy to aging | ◎ | 200 |
CPVC | 氯乙烯 | 1.65 | Mouse Grey | <0.05 | gradually aging | ◎ | X |
HDPE | PE | 1 | White | <0.01 | long-term aging | ◎ | 2.3-2.35 |
UPE | 乙烯鋼 | 1 | White | <0.01 | long-term aging | ◎ | 2.2 |
PVDF | 鐵氟龍2F | 1.8 | White | 0.04 | Unchanged | ◎ | 8.0 |
PTFE | 鐵氟龍4F | 2.2 | White | <0.01 | Unchanged | ◎ | 2.0 |
PETP | 聚酯膠 | 1.38 | White | 0.3 | Unchanged | ◎ | X |
PP | 聚丙烯 | 1 | White | 0.02-0.03 | long-term aging | ○ | 2.65 |
Note: ◎Excellent ○Be △Fair ╳Poor
FEATURES | PHYSICAL | ||||||
GENERIC | COMMON NAME | PROPORTION | IN THEIR ORIGINAL APPEARANCE | WATER ABSORPTION | CHANGES WHEN EXPOSED TO LIGHT | MACHINABILITY | YUDEN RATE |
Test Mode | ASTM | D790 | Common Materials | D572 | D150 | ||
單位 | Target | 24Hrs % | 1KHz | ||||
AP-6 | 尼龍6 | 1.15 | White | 1.6 | Yellow | ○ | 4.0-4.9 |
AP-66 | 尼龍66 | 1.15 | Light earth tones | 1.5 | Yellow | ○ | 3.9-4.5 |
MC | MC尼龍 | 1.15 | White | 0.6-2.0 | Yellow | ○ | 3-7 |
POM | 塑膠鋼 | 1.42 | White | 0.22 | long-term aging | ◎ | 3.8 |
ABS | 丁二烯 | 1.07 | translucent | 0.1-0.8 | easy to aging | ○ | 2.4-4.75 |
PMMA | 壓克力 | 1.20 | translucent | 0.3-0.4 | easy to aging | ○ | 3.0-3.5 |
PC | 聚碳酸酯 | 1.20 | Dark brown | 0.15 | Unchanged | ◎ | 3.02 |
PEEK | 聚醚醚酮 | 1.26-1.32 | black | 0.14 | long-term aging | ◎ | 3.4 |
BAKELITE | 電木 | 1.5 | Brown | 1.5 | Unchanged | △ | X |
FRP | 玻璃纖維 | 2.0 | Light gray | 0.1-1.0 | Unchanged | X | X |
Note: ◎Excellent ○Be △Fair ╳Poor
FEATURES | MECHANICAL | ||||||||
GENERIC | COMMON NAME | HARDNESS | TENSILE STRENGTH | ELONGATION | TENSILE ELASTIC MODULUS | COMPRESSIVE STRENGTH | BENDING STRENGTH | IMPACT STRENGTH | |
Test Mode | ASTM | D785 | D638 | D695 | D790 | IZOD | |||
Units | kg/cm2 | ||||||||
PVC | 氯乙烯 | R108-118 | 350-630 | 2.0-4.0 | 2.5-4.2 | 560-910 | 200 | 1.0-3.0 | |
CPVC | 氯乙烯 | R117-122 | 527-633 | 4.5-6.5 | 2.53-3.34 | 633-1550 | X | 5.44-30.5 | |
HDPE | 聚乙烯 | R38-50 | 220-390 | 15-100 | 0.42-1.00 | 330 | 2.3-2.35 | 8.2-10.9 | |
UPE | 乙烯鋼 | R40-50 | 400-470 | 300-500 | 0.20-1.10 | 230 | 2.2 | 不破壞 | |
PVDF | 鐵氟龍2F | SHORE D 80 | 490 | 100-300 | 0.84 | 700 | 8.0 | 19.0 | |
PTFE | 鐵氟龍4F | SHORE D 50-60 | 140-320 | 200-400 | 0.41 | 120 | 2.0 | 16.4 | |
PETP | 聚酯膠 | M70-115 | 1200-1760 | 70-130 | 3.2-4.2 | 914-211 | X | 70 | |
PP | 聚丙烯 | R90-100 | 350-360 | 3-20 | 2.1-3.6 | 490 | 2.65 | 2.2-16.3 |
FEATURES | MECHANICAL | ||||||||
GENERIC | COMMON NAME | HARDNESS | TENSILE STRENGTH | ELONGATION | TENSILE ELASTIC MODULUS | COMPRESSIVE STRENGTH | BENDING STRENGTH | IMPACT STRENGTH | |
Test Mode | ASTM | D785 | D638 | D695 | D790 | IZOD | |||
Units | kg/cm2 | ||||||||
AP-6 | 尼龍6 | R103-118 | 490-860 | 2.5-320 | 1.1-2.7 | 500-910 | 4.0-4.9 | 5.5-19.6 | |
AP-66 | 尼龍66 | R108-118 | 630-840 | 60-300 | 1.2-2.9 | 470-880 | 3.9-4.5 | 5.5-10.9 | |
MC | MC尼龍 | R112-120 | 670-840 | 360-320 | 3.5-4.5 | 770-980 | 3-7 | 223 | |
POM | 塑膠鋼 | M78-80 | 620 | 60-75 | 2.8 | 1120 | 3.8 | 6.5-7.6 | |
ABS | 丁二烯 | R80-118 | 170-630 | 10-140 | 0.7-2.9 | 188-177 | 250-950 | 3.8-66 | |
PMMA | 壓克力 | M84-105 | 490-770 | 2-10 | 3.2 | 840-0 | 900-1300 | 2.6-7 | |
PC | 聚碳酸酯 | M70-R118 | 560-670 | 60-100 | 2.5 | 880 | 950 | 65-87 | |
PEEK | 聚醚醚酮 | SHORE D 88 | X | 50 | 1.1 | 900 | 1700 | 8.3 | |
BAKELITE | 電木 | E79-82 | 211-633 | 0.37-0.57 | X | 17-35 | 1200-1500 | 2.0-4.0 | |
FRP | 玻璃纖維 | M100-105 | 1400-4200 | 4 | 14-28 | 3500-4900 | 4900-7000 | 109-163 |
FEATURES | CHEMICAL | |||||
GENERIC | COMMON NAME | WEAK ACID CHANGE | ACID CHANGE | WEAK BASE CHANGE | BASE CHANGE | EFFECT OF ORGANIC SOLVENT |
Test Mode | D543 | |||||
PVC | 氯乙烯 | △ | △ | ○ | ○ | ○ |
CPVC | 氯乙烯 | ○ | ○ | ◎ | ◎ | ○ |
HDPE | 聚乙烯 | ◎ | △ | ◎ | ◎ | ○ |
UPE | 乙烯鋼 | ◎ | ◎ | ◎ | ◎ | ◎ |
PVDF | 鐵氟龍2F | ◎ | △ | ◎ | △ | ◎ |
PTFE | 鐵氟龍4F | ◎ | ◎ | ◎ | ◎ | ◎ |
PETP | 聚酯膠 | ◎ | ◎ | ◎ | ◎ | ◎ |
PP | 聚丙烯 | ◎ | △ | ◎ | ◎ | ○ |
AP-6 | 尼龍6 | ○ | X | ◎ | ◎ | ○ |
AP-66 | 尼龍66 | ○ | X | ◎ | ◎ | ○ |
MC | MC尼龍 | ○ | △ | ○ | ○ | ○ |
POM | 塑膠鋼 | △ | X | ◎ | ◎ | ◎ |
ABS | 丁二烯 | ○ | △ | ○ | ○ | X |
PMMA | 壓克力 | ○ | △ | ○ | X | X |
PC | 聚碳酸酯 | ◎ | △ | ○ | X | △ |
PEEK | 聚醚醚酮 | ◎ | ◎ | ◎ | ◎ | ◎ |
BAKELITE | 電木 | △ | △ | △ | △ | △ |
FRP | 玻璃纖維 | △ | △ | △ | △ | △ |
Note: ◎Excellent ○Be △Fair ╳Poor
FEATURES | ELECTRICA | ||||
GENERIC | COMMON NAME | ARC RESISTANCE | DIELECTRIC STRENGTH | DIELECTRIC PROPERTIES | VOLUME RESISTANCE RATIO |
Test Mode | ASTM | D495 | D149 | D150 | D257 |
Units | Sec | kv/mm | 1KHz | Ω-CM | |
PVC | 氯乙烯 | X | 14 | 200 | 1016 |
CPVC | 氯乙烯 | X | 1.22-1.50 | X | 1015 |
HDPE | 聚乙烯 | 200-235 | 17.7-19.7 | 2.3-2.35 | 1016 |
UPE | 乙烯鋼 | X | 50 | 2.2 | 1013 |
PVDF | 鐵氟龍2F | 50-70 | 10.2 | 8.0 | 2 x 1014 |
PTFE | 鐵氟龍4F | >200 | 18.9 | 2.0 | >1013 |
PETP | 聚酯膠 | 125 | 18.0 | X | 1019 |
PP | 聚丙烯 | 120 | 19.7-260 | 2.65 | 2 x 1016 |
AP-6 | 尼龍6 | 135 | 17.3-20.0 | 4.0-4.9 | 1012- 1015 |
AP-66 | 尼龍66 | 130-140 | 15.1-18.5 | 3.9-4.5 | 1014- 1015 |
MC | MC尼龍 | X | 12-20 | 3-7 | 1012- 1015 |
POM | 塑膠鋼 | 240 | 18.3 | 3.8 | 1014 |
ABS | 丁二烯 | 47-87 | 12.2-16.1 | 2.4-4.75 | 1016 |
PMMA | 壓克力 | X | 17.7-21.6 | 3.0-3.5 | >1014 |
PC | 聚碳酸酯 | 10-120 | 15-7 | 3.02 | 2 x 1011 |
PEEK | 聚醚醚酮 | 4.8 | 190 | 3.4 | 5 x 1016 |
BAKELITE | 電木 | 2-130 | 200-400 | X | 5 x 107 |
FRP | 玻璃纖維 | 120-180 | 300-400 | X | >1013 |